Showing 4 results for Microhardness
H. Arabi, S. Rastegari, V. Ramezani, Z. Valefi,
Volume 10, Issue 2 (6-2013)
Abstract
The objectives of this research were to find an economical way of reducing porosities in the microstructure of coatings deposited by flame spraying technique on CK45 steel and also trying to increase their cohesive strength to the substrate, so that the overall wear properties of this type of coating can be improved. So several specimens from this steel coated with NiCrBSi powder under specific conditions were subjected to various furnace heat treatment at 1000, 1025, 1050, 1075 and 1100 °C, each for periods of 5, 10 and 15 minute before cooling them in air. Tribological properties of treated coatings were evaluated by pin on disc method. The results show the highest wear resistance and microhardness values observed in one of the sample was due to lower amount of porosity and higher amount of very fine Cr2Ni3B6 particles precipitated homogeneously throughout its microstructure during specific heat treatment.
Z. Ghaferi, S. Sharafi, M.e. Bahrololoom,
Volume 14, Issue 2 (6-2017)
Abstract
In this research, nanocrystalline Co-Fe coatings were electrodeposited on copper substrate. The influence of current density on different properties of the films at two pH levels was investigated. All the coatings showed nodular structure with rougher morphology at higher current densities. Due to anomalous deposition at higher current density, the amount of iron content increased and reached its maximum value at about 50 wt.% for the coating obtained from pH 5. X-ray diffraction patterns showed hcp structure as the dominant phase. However, by increasing current density at lower pH value, a double phase structure containing fcc+hcp phases was detected. It was observed that current density has a positive effect on grain refinement. However, coarser grains would obtain at lower pH value. Microhardness measurements showed that, there is a direct relationship between grain size and microhardness. Moreover, microstructure in double phase structure films can influence microhardness more dominantly. Vibrating sample magnetometer (VSM) measurements indicated that the saturation magnetic is proportion to deposited iron content and reached its maximum value at about 1512 emu/cm3. It was cleared that grain size, phase structure and chemical composition can affect coercivity of the films effectively.
M. Hoghooghi, O. Jafari, S. Amani, G. Faraji, K. Abrinia,
Volume 16, Issue 4 (12-2019)
Abstract
Spread extrusion is a capable method to produce different samples with a wider cross-section from the smaller billets in a single processing pass. In this study, dish-shaped samples are successfully produced from the as-cast cylindrical AM60 magnesium alloy at 300 °C, the mechanical properties and microstructural changes of the final specimens are precisely evaluated. Due to the high amount of plastic strain, which is applied to the initial billet during the material flow in the expansion process, grain refinement occurred as a result of recrystallization and subsequently good mechanical properties achieved. Therefore, mean grain size reduced from 160 µm to 14 µm and initial equiaxed grains changed to the elongated ones surrounded by fine grains. Also, microhardness measurements indicate that hardness increased from 51 Hv to 70 Hv. Some fluctuations were also observed in the hardness profile of the sample which was mainly related to the bimodal structure of the final microstructure. Good mechanical properties, fine microstructure, and also the ability to produce samples with higher cross-section make the spread extrusion process a promising type of extrusion.
Sa. Benkacem, K. Boudeghdegh, F. Zehani, Y. Belhocine,
Volume 17, Issue 2 (6-2020)
Abstract
This paper focuses on the effect of ZrSiO4/ZnO ratio on the properties of the glaze to be used on ceramic sanitary-ware. Structural and morphological characterization of these glazed ceramics were identified by XRD, SEM, FTIR and Raman Spectroscopy. Furthermore, thermal properties were determined by DTA and TG techniques. Besides, flexural strength, Vickers Microhardness, whiteness and chemical resistance were investigated experimentally. XRD analysis showed that the zircon and quartz were the crystalline phases, zircon was also precipitated into the glaze layer during firing. It was found that an increase of the ZrSiO4/ZnO ratio part weights from 3.85 to 67, causes an increase in the zircon crystallite particle size from 203.90 to 288.86 Å. From DTA, it was observed that by increasing ZrSiO4/ZnO ratio, the crystallization temperature of zircon decreases. The glaze exhibits the highest whiteness value when the ratio of ZrSiO4/ZnO becomes 12.60.