Showing 4 results for Sima
M. Amuei, M. Emamy, R. Khorshidi, A. Akrami,
Volume 12, Issue 3 (9-2015)
Abstract
In this study, Al2014 alloy refined with Al-5%Ti-1%B master alloy was prepared by strain-induced melt
activated (SIMA) process. The main variables of the SIMA process were cold working, holding time and temperature in
semi-solid state. Cold working was applied on specimens by upsetting technique to achieve 10%, 20% and 30% height
reduction. Cold worked specimens were heat treated in semi-solid state at 585 °C, 595 °C, 605 °C, 615 °C, 625 °C and
635 °C and were kept in these temperatures for different times (20 and 30 min). Observations through optical and
scanning electron microscopy were used to study the microstructural evaluation. The results revealed that fine and
globular microstructures are obtained by applying 30 % height reduction percentage and heat treating in 625 °C for
30 min. Comparison between refined and unrefined Al2014 alloy after applying SIMA process showed that Al-5%Ti-1%B master alloy has no significant effect on average globule size but makes the final structure more globular.
M. Alipour, M. Emami, R. Eslami Farsania, M. H. Siadati, H. Khorsand,
Volume 12, Issue 4 (12-2015)
Abstract
A modified strain-induced melt activation (SIMA) process was applied and its effect on the structural characteristics and hardness of the aluminum alloy Al–12Zn–3Mg–2.5Cu was investigated. Specimens subjected to a deformation of 40% at 300 °C were heat treated at various times (10-40 min) and temperatures (550-600 °C). Microstructural studies were carried out using optical and scanning electron microscopies (SEM). Results showed that the best microstructure was obtained at the temperature and time of 575 °C and 20 min, respectively. The hardness test results revealed superior hardness in comparison with the samples prepared without the application of the modified SIMA process.
T6 heat treatment including quenching to 25 °C and aging at 120 °C for 24 h was employed to reach to the maximum strength. After the T6 heat treatment, the average tensile strength increased from 231 MPa to 487 and 215 MPa to 462 for samples before and after strain-induced melt activation process, respectively. Ultimate strength of globular microstructure specimens after SIMA process has a lower value than as-cast specimens without SIMA process
M. Hamdi, H. Saghafian Larijani, S. G. Shabestari, N. Rahbari,
Volume 17, Issue 3 (9-2020)
Abstract
Aluminum matrix composites are candidate materials for aerospace and automotive industries owing to their specific properties such as high elastic modulus (E), improved strength and low wear rate. The effect of thixoforming process on the wear behavior of an Al-Mg2Si composite was studied in this paper. During applying thixoforming process, casting defects such as macrosegration, shrinkage and porosity are being effectively reduced. These advantages are sufficient to attract more exploration works of thixoforming operation. Thermal analysis of the composite, as-cast microstructure, wear surface and subsurface area of the thixoformed alloy were investigated. Wear behavior of the specimens were examined using a pin-on-disk machine based on ASTM-G99, at the applied loads of 25, 50 and 75 N and the constant sliding velocity of 0.25m/s. The worn surfaces and subsurfaces were examined by scanning electron microscopy (SEM). The experimental results indicated that the thixoformed specimens exhibited superior wear resistance than the as-cast alloy. Moreover, the dominant wear mechanism is an adhesive wear followed by the formation of a mechanical mixed layer (MML). However, a severer wear regime occurs in the as cast specimens compared with the thixoformed ones
Mohammad Alipour,
Volume 20, Issue 1 (3-2023)
Abstract
The effect of Strain-Induced Melt-Activated (SIMA) Process, ultrasonic treatment (UST) and Al-5Ti-1B refiner on the microstructure and globularity of Al–15%Mg2Si composite was studied. Deformation of 25% were used. After deformation the samples were heated at 560, 580 and 595 °C for 5, 10, 20 and 40 min. The composite was treated with different amounts of the Ti concentrations and ultrasonic treatment with different power. Microstructural study was carried out on the alloy. It was observed that SIMA process, ultrasonic treatment and Al-5Ti-1B refiner has caused the globular morphology of Mg2Si particles. The results showed that for the desired microstructures of the alloy during SIMA process, the optimum temperature and time are 595 °C and 20 min respectively. Optimum amount of Ti refiner is 1 wt.% and power for UST is 1800W. After applying the SIMA process, Al-5Ti-1B master alloy and ultrasonic treatment, the strength and engagement have increased. This means that tensile strength increases from 251 MPa to 303 MPa and elongation percentage improves from 2.1 to 3.4, respectively.