Mirfakhraee B., Eshraghi H., Sar Poulaki H.,
Volume 2, Issue 1 (Oct 2005)
Abstract
Effect of MgO addition on reaction sintering of aluminium titanate was investigated using equimolar Al2O3 and TiO2 after firing the samples at 1400 C for four hours. Results showed that MgO addition enhanced the sintering process by magnesium aluminates formation, which led to lower porosity and improved densification of the samples. Physical and mechanical properties showed that samples containing 5 wt% MgO was the optimum composition.
Baradari H., Amani Hamedani H., Karimi Khoygani S., Rezaei H.r., Javadpour J., Sar Poulaki H.,
Volume 3, Issue 1 (Oct 2006)
Abstract
Ultrafine hydroxyapatite (HAp) powders with crystallite size in the range of 10-90 nm were synthesized by chemical precipitation process using Ca(OH)2 and H3PO4 solutions as starting materials. Molar ratio of Ca/P=1.68 was kept constant throughout the process and alkaline condition for the reaction was maintained using ammonium hydroxide. The role of raw material concentration on HAp crystallite size and morphology were investigated using X-ray diffraction (XRD) and scanning electron microscope (SEM) techniques. The results revealed that variations in crystallite size and morphology of synthesized HAp are strongly affected by the concentration of acid solution. To study the sintering behavior of HAp particles, the powders were pressed at 200 MPa using a uniaxial press. Sintering experiments were carried out at temperatures of 1100, 1250 and 1300°C with various soaking times at maximum temperatures. XRD was also used in determining thephases present after sintering process. The results indicated the decomposition of HAp into a-tricalcium phosphate (TCP) and b-TCP phases at 1300°C. The microstructure of the sintered HAp ceramics was characterized by SEM.